PENGARUH KOMPOSISI BAHAN PADUAN ALUMUNIUM, TEMBAGA, DAN SENG TERHADAP KEKERASAN LOGAM TIMAH

Muhammad Andrew Juliendi, Anugrah Agung Ramadhan

Abstract


Alloyed metals play a crucial role in industry due to their superior mechanical properties compared to pure metals. One commonly used industrial metal is tin (Sn), which, despite its corrosion resistance and low melting point, exhibits relatively low hardness. To enhance its mechanical properties—particularly hardness—alloying with other metals such as aluminum (Al), copper (Cu), and zinc (Zn) is performed. These alloying elements are chosen for their ability to improve strength, durability, and performance in various applications, especially in metal casting processes. Metal casting is a key manufacturing technique in which molten metal is poured into a mold to produce a desired shape. In this study, a Brinell hardness test was conducted to evaluate the effect of these alloying elements on improving the hardness of tin. The results of this research are expected to contribute to the development of stronger, more durable, and efficient alloy materials for modern industrial needs

 

Logam paduan memiliki peranan penting dalam industri karena menawarkan sifat mekanik yang lebih unggul dibanding logam murni. Salah satu logam yang banyak digunakan dalam industri adalah timah (Sn), yang meskipun memiliki ketahanan korosi dan titik leleh rendah, namun kekerasannya tergolong rendah. Untuk meningkatkan sifat mekaniknya, terutama kekerasan, dilakukan proses pemaduan dengan logam lain seperti aluminium (Al), tembaga (Cu), dan seng (Zn). Paduan ini bertujuan untuk memperbaiki kekuatan, daya tahan, dan performa logam dalam berbagai aplikasi, khususnya dalam proses pengecoran logam. Pengecoran logam merupakan teknik manufaktur penting dalam pembentukan produk berbahan logam, di mana logam cair dituangkan ke dalam cetakan untuk memperoleh bentuk yang diinginkan. Dalam penelitian ini, dilakukan pengujian kekerasan menggunakan metode Brinell guna mengevaluasi pengaruh paduan terhadap peningkatan kekerasan timah. Hasil dari penelitian ini diharapkan dapat memberikan kontribusi terhadap pengembangan material paduan yang lebih kuat, tahan lama, dan efisien untuk kebutuhan industri modern.


Keywords


Achmad Dodo, S. (2020). Pengaruh variasi tekanan dan suhu pada pengadukan serbuk aluminium (Al), magnesium (Mg), dan seng (Zn) terhadap sifat mekanik logam dengan metode metalurgi serbuk. Jurnal Dinamis, 8(2). Elbar, W., & Tampubolon, K. (2020). \376\377\

Full Text:

PDF

References


Achmad Dodo, S. (2020). PENGARUH VARIASI TEKANAN DAN SUHU PADA PENGADUKAN SERBUK ALUMINIUM (Al), MAGNESIUM (Mg), DAN SENG (Zn) TERHADAP SIFAT MEKANIK LOGAM DENGAN METODE METALURGI SERBUK. Jurnal Dinamis, 8(2).

Elbar, W., & Tampubolon, K. (2020). 37637700900_00I00D00 00400000700000 00 00J00M00E00M00M00E00 00V00400N00200 00D00e00s00 002000002000. JMEMME, 4(2). https://doi.org/10.31289/jmemme.v4i2.4070

Fisika, P., Sains dan Teknologi, F., Alauddin Makassar, U., Risqi Adikaning Rani, S., & Nurrahmi, S. (2021). JURNAL SAINS FISIKA METODE HEAT TREATMENT PADA PENGUJIAN KEKERASAN LOGAM ALUMINIUM DENGAN VARIASI MEDIA PENDINGIN. In Jurnal Sains Fisika (Vol. 1). http://journal.uin-alauddin.ac.id/index.php/sainfis

Gultom, S., Ramadhan, A., & Mawardi, M. (2022). Analisis pengecoran timah murni terhadap laju korosi. Jurnal VORTEKS, 3(2), 247–250. https://doi.org/10.54123/vorteks.v3i2.216

Helanianto, H., Epriyandi, E., & Rahmadi, H. (2020). PENGARUH VARIASI ARUS PENGELASAN SMAW TERHADAP KEKERASAN LOGAM INDUK DAN LOGAM LAS. ELEMEN : JURNAL TEKNIK MESIN, 7(2), 138–147. https://doi.org/10.34128/je.v7i2.148

Lestari, F. P., Kartika, I., Juwono, A. L., & Anawati, A. (2022). Kajian Komposit Berbasis Paduan Logam Magnesium Berpenguat Keramik untuk Aplikasi Ortopedi. TEKNIK, 43(3), 236–253. https://doi.org/10.14710/teknik.v43i3.46575

Malik, I., Yunus, M., Arnoldi, D., Fernandes, E., Prodi, ), Tmpp, D.-I., Mesin, T., & Sriwijaya, P. N. (2021). PENGENALAN PENGGUNAAN SIMULASI PENGECORAN BAGI USAHA COR LOGAM DI PALEMBANG. 4(4). https://doi.org/10.36257/apts.vxix

Naafila, A., Purnowidodo, A., Setyarini, H., Jurusan, D., & Mesin, T. (2019). Pengaruh Waktu Solution Treatment Terhadap Kekuatan Tarik Aluminium Paduan AA 7075-T6.

Nasoha, M., Alam, J. B., & Alam, S. (n.d.). Pengaruh Variasi Tekanan Torsi Terhadap Uji Kekerasan Brinell Dan Uji Mikrostruktur Pada Aluminium 6061 Menggunakan Metode Friction Welding.

Primayoga, *, Sowiyk, H., & Bayuseno, A. P. (2016). PENGARUH PENAMBAHAN UNSUR TIMAH (Sn) TERHADAP SIFAT FISIS DAN MEKANIS PADA MATERIAL BEARING BERBAHAN DASAR ALUMINIUM (Al) HASIL PENGECORAN HPDC. In Jurnal Teknik Mesin S-1 (Vol. 4, Issue 3).

Syukur Alfauzi, A., Purnomo, A., Tjahjono, B., sa, N., Program Studi Teknik Mesin, adah, Teknik Mesin, J., Negeri Semarang JlProfHSudarto, P., & Tembalang, S. (2019a). Pembuatan Roda Gigi dari Bahan Serbuk Logam Tembaga dan Alumunium dengan Proses Kompaksi. In Jurnal Rekayasa Mesin (Vol. 14, Issue 3). https://jurnal.polines.ac.id/index.php/rekayasa

Syukur Alfauzi, A., Purnomo, A., Tjahjono, B., sa, N., Program Studi Teknik Mesin, adah, Teknik Mesin, J., Negeri Semarang JlProfHSudarto, P., & Tembalang, S. (2019b). Pembuatan Roda Gigi dari Bahan Serbuk Logam Tembaga dan Alumunium dengan Proses Kompaksi. In Jurnal Rekayasa Mesin (Vol. 14, Issue 3). https://jurnal.polines.ac.id/index.php/rekayasa

Wibawa Perdana, W. (2019). ANALISIS LOGAM BERAT DI KEMASAN KALENG. 9(2).




DOI: https://doi.org/10.17509/e.v24i2.83131

Refbacks

  • There are currently no refbacks.


Copyright (c) 2025 EDUTECH

Lisensi Creative Commons
Ciptaan disebarluaskan di bawah Lisensi Creative Commons Atribusi-BerbagiSerupa 4.0 Internasional.
Copyright © 2018 Edutech