ANALISIS PENGARUH KONDISI PENYIMPANAN ELEKTRODA LOW HIDROGEN E7018 TERHADAP CACAT LAS DENGAN INSPEKSI NON-DESTRUCTIVE TEST
Abstract
This study aims to (1) determine the effect of electrode storage conditions on the resulting welding defects, (2) determine the effect of different electrode storage locations on welding results, and (3) determine what types of welding defects are produced by E7018 electrodes that have been given several treatments. The method used in this study is an experiment, the number of samples made as many as 4 samples is divided into 4 variations of electrode storage conditions using low-carbon steel, namely ST 37. Testing consists of a non-destructive test or a non-destructive test using, the results of this study are that the condition of electrodes stored in various conditions in a span of one week affects the resulting welding defects, the difference in the storage of electrodes affects the welding results, electrodes stored indoors and outdoors will cause more welding defects compared to electrodes stored in insulin and also electrodes that are newly opened from the packaging, The characteristics of the E7018 low hydrogen electrode in indoor and outdoor storage conditions are moist while the E7018 low hydrogen electrode in the storage conditions of insulin and the new electrodes of the packaging are dry.
Penelitian ini bertujuan untuk (1) mengetahui pengaruh kondisi penyimpanan elektroda terhadap cacat pengelasan yang dihasilkan, (2) mengetahui pengaruh perbedaan tempat penyimpanan elektroda terhadap hasil pengelasan, dan (3) mengetahui jenis cacat las apa saja yang dihasilkan oleh elektroda E7018 yang sudah diberi beberapa perlakuan. Metode yang digunakan dalam penelitian ini adalah experiment, jumlah pembuatan sampel sebanyak 4 sampel dibagi menjadi 4 variasi kondisi penyimpanan elektroda dengan menggunakan baja berkarbon rendah yaitu ST 37. Pengujian terdiri dari uji tanpa merusak atau non destructive test menggunakan. Hasil penelitian ini adalah kondisi elektroda yang disimpan pada berbagai kondisi dalam rentang waktu satu minggu berpengaruh terhadap cacat pengelasan yang dihasilkan, perbedaan tempat penyimpanan elektroda berpengaruh pada hasil pengelasan, elektroda yang disimpan didalam dan luar ruangan akan menimbulkan lebih banyak cacat las dibandingkan dengan elektroda yang disimpan di dalam insulin dan juga elektroda yang baru di buka dari kemasan, karakteristik elektroda low hydrogen E7018 pada kondisi penyimpanan di dalam dan di luar ruangan elektroda bersifat lembab sedangkan elektroda low hydrogen E7018 pada kondisi penyimpanan di dalam insulin dan elektroda yang baru dari kemasan bersifat kering.
Keywords
Full Text:
PDFReferences
Afan, M. Bin, Purwantono, Mulianti, & Rahim, B. (2020). Pengaruh Suhu Penyimpanan Elektroda Low Hydrogen E7016 terhadap Hasil Uji Tekuk Sambungan Las Pelat Baja Karbon SS400. Jurnal Rekayasa Mesin, 15(1), 20–25. https://jurnal.polines.ac.id/index.php/rekayasa
Agus S, & Pramono. (2021). Teknik Pengelasan Busur Manual (SMAW) SMK/MAK Kelas XI. Program Keahlian Teknik Mesin. Kompetensi Keahlian Teknik Pengelasan. Penerbit Andi. https://books.google.co.id/books?id=YCgqEAAAQBAJ
Akhmadi, A. N., & Qurohman, M. T. (2020). Analisa Hasil Pengelasan 2g Dan 3g Dengan Bahan Plat Besi St 40 Ketebalan 10 mm Dan Voltase 20 - 35 Menggunakan Mesin Las Mig. Nozzle : Journal Mechanical Engineering, 9(2), 25–30. https://doi.org/10.30591/nozzle.v9i2.2259
Antaqiya, F. M. A., Budiarto, U., & Jokosisworo, S. (2019). Analisa Pengaruh Variasi Proses Preheating Pada Pengelasan Shielded Metal Arc Welding (SMAW) Terhadap Kekuatan Tarik dan Struktur Mikro Baja ST 60. Jurnal Teknik Perkapalan, 7(4), 334–344.
Aqdar Fitrah, M., Balfas, M., & Mardin. (2021). Analisis Cacat Las Hasil Pengelasan Kombinasi GTAW Dan SMAW Posisi 6G Pada Pipa SA 106 Grade B. JMove: Jurnal FT Lama, 3(1), 1–5.
Ariyanto Ariyanto. (2024). Analisa Pengaruh Arus Listrik Pengelasan Gmaw Alumunium 5052. Jurnal Ilmiah Teknik, 3(1), 38–43. https://doi.org/10.56127/juit.v3i1.1159
Azis, R. A., Suharno, S., & Saputro, H. (2019). Pengaruh Variasi Diameter Elektroda E7018 Terhadap Kekuatan Tarik, Kekerasan, dan Struktur Mikro Pengelasan pada Baja Karbon Rendah Jenis SS400 dengan Metode SMAW. Jurnal Teknik, 17(2), 94–105. https://doi.org/10.37031/jt.v17i2.53
Azmi, Hadiguna, R. A., Jonrinaldi, & Ramadhianto, A. (2023). Optimalisasi Parameter Teknik Pengelasan Shielded Metal Arc Welding (SMAW) dengan Menggunakan Metode Taguchi. Prosiding Seminar Nasional Teknik Industri (SENASTI), 860–869. www.kobelcocm-global.com
Azwinur;, & Muhazir. (2021). PENGARUH JENIS ELEKTRODA PENGELASAN SMAW TERHADAP SIFAT MEKANIK MATERIAL SS400. 19–25.
Bakhori, A. (2017). Perbaikan Metode Pengelasan Smaw (Shield Metal Arc Welding) Pada Industri Kecil Di Kota Medan. Buletin Utama Teknik, 13(1), 14–21.
Bakhori, A. (2021). Analisa Cacat Hasil Pengelasan Pada Baja Krbon Rendah Terhadap Pengaruh Masukan Panas Las. Semnastek Uisu, 0–5.
Banggur, P. G., & Rosidah, A. A. (2024). Analisis Pengaruh Jenis Kampuh dan Diameter Elektroda pada Pengelasan SMAW Baja AISI 1045 terhadap Ketangguhan dan Laju Korosi. Prosiding SENASTITAN: Seminar …, Senastitan Iv, 1–7.
Bin Afan, M., Rahim Jurusan Teknik Mesin, B., Teknik, F., & Negeri Padang Jl Hamka, U. (2020). Pengaruh Suhu Penyimpanan Elektroda Low Hydrogen E7016 terhadap Hasil Uji Tekuk Sambungan Las Pelat Baja Karbon SS400. Jurnal Rekayasa Mesin, 15(1), 20–25.
Budhi Susetyo, F., Amirudin, J., & Yudianto, V. (2013). Studi Karakteristik Pengelasan Smaw Pada Baja Karbon Rendah St 42 Dengan Elektroda E 7018. Jurnal Konversi Energi Dan Manufaktur, 1(1), 32–39. https://doi.org/10.21009/jkem.1.1.4
Ginting, B. B. (2023). Analisa Kekuatan Tarik Pengelasan SMAW pada Material Baja Hardox Steel 450. Prodi Teknik Mesin, Jurusan Teknik Mesin, Politeknik Negeri Medan, 7(2), 7584–7590.
Gumono, G., Hadi, S., & Irawan, B. (2018). Perbandingan Suhu Penyimpanan Elektroda Terhadap Kekerasan Baja Karbon. Info-Teknik, 19(1), 15. https://doi.org/10.20527/infotek.v19i1.5139
Irwansyah. (2019). Deteksi Cacat Pada Material Dengan Teknik Pengujian Tidak Merusak. Lensa, 2(48), 7–14.
Karmawan, W., Adja, H. B., Alvindo, N. V, Handoko, K. T., Pradana, J., Zakkaria, L. N., Zuhron, M., Jaya, H. T. S., & Subardi, A. (2020). Analisa kekuatan variasi arus las SMAW dengan elektroda E 7018 bahan baja ST 42 terhadap sifat mekanis. Jurnal JMMME, 1(2), 19.
Mamurung, R. D. N., Budiarto, U., & Yudo, H. (2021). Analisa Kekuatan Tarik dan Impak Hasil Las SMAW (Shielded Metal Arc Welding) Pada Baja ASTM A36 Dengan Variasi Polaritas dan Besar Arus Pengelasan. Jurnal Teknik Perkapalan, 9(4), 360.
Ma’sum, M. A., Usman, M., & Fakhrurozi, M. (2025). Pengaruh Parameter Arus, Polaritas, Dan Diameter Elektroda Terhadap Cacat Las Pada Pengelasan Smaw Dengan Material Baja ST37. Jurnal Ilmiah Teknik Mesin, 11(1), 63–68. http://ejournal2.uika-bogor.ac.id/index.php/ame/index
Munawar Muthia, H., Gusniar Nugraha, I., & Hanafi, R. (2023). Pengaruh Jenis Elektroda Las SMAW Terhadap Sifat Mekanik dan Struktur Mikro. Jurnal Pendidikan Teknik Mesin Undiksha, 11(1), 93–110.
Pratama, O. Y., & Yunus, Y. (2024). Analisa Pengaruh Variasi Kuat Arus Dan Diameter Elektroda Metode Pengelasan Smaw Pada Material Stainless Steel 304 Terhadap …. Jurnal Teknik Mesin, 7–16.
Pratama, R. Y., Basuki, M., & Pranata, E. (2020). Pada Material Baja Kapal SS 400 Terhadap Cacat Pengelasan. Seminar Teknologi Kebumian Dan Kelautan (SEMITAN II), 203–209.
Pratiwi, Y. R., & Wibowo, S. S. (2019). Pengaruh Jenis Elektroda Dan Jumlah Pass Terhadap Uji Kekerasan Hasil Pengelasan Dan Struktur Mikro Pada Proses Pengelasan Shielded Metal Arch Welding. Briliant: Jurnal Riset Dan Konseptual, 4(2), 159. https://doi.org/10.28926/briliant.v4i2.287
Puspitasari, E., Jannah, R. M., Sipil, J. T., Teknik, F., Tidar, U., & Utara, M. (2022). Prosiding Seminar Nasional Riset Teknologi Terapan : 2022 . Jurnal Riset Teknologi Terapan.
Rokhmanto, F. (2020). PENGENALAN TEKNIK PENGELASAN LOGAM SEBAGAI PELUANG WIRAUSAHA MASYARAKAT. PENDAHULUAN Melalui Program Pengabdian Masyarakat yang dilaksanakan Dosen Teknik Mesin Unpam sebagai manusia yang berintelektual tinggi diharapkan dapat memberikan konstribusi yang n. PENGENALAN TEKNIK PENGELASAN LOGAM SEBAGAI PELUANG WIRAUSAHA MASYARAKAT.
Satria Dwi Putra ,Teknik, F., Surabaya, U. N., Mesin, P. T., Teknik, F., & Surabaya, U. N. (2023). ANALISA PENGARUH ARUS PENGELASAN SMAW E7018 PADA BAJA ASTM A588 Satria Dwi Putra Novi Sukma Drastiawati Abstrak. Jurnal Teknik Mesin.
Setyawan, C. W., Syaripuddin, Lubi, A., & Susetyo, F. B. (2022). Pengaruh Suhu Pengeringan Elektroda E 7018 Terhadap Hasil Pengelasan Material A36 Drying Temperature Effect of E 7018 Electrode on Weld Joint of A36 Material. Jurnal Asiimetrik: Jurnal Ilmiah Rekayasa Dan Inovasi, 4(2), 209–220.
Sitepu, N., & Sukino, S. (2021). Analisa Kekuatan Tarik Terhadap Jumlah Layer Pada Proses Pengelasan Kombinasi Gtaw Dan Smaw Sambungan St37 Posisi 3G. Jurnal Teknologi Mesin UDA, 2(1), 151–159.
Soedarmadji, W. (2020). Pengaruh Pengelasan Shielded Metal Arc Welding (SMAW) pada Mild Steel S45C di Daerah HAZ dengan Pengujian Metalografi. Mechanical and Manufacture Technology, 1(1), 12–17.
Studi, P., Manufaktur, T., Batulicin, P., & Selatan, K. (2024). Pengaruh variasi kampuh pengelasan smaw terhadap kekuatan tarik pada baja karbon s50c. 12(2), 79–83.
Sudiyanto, A., Mirahati, R. Z., & Rahma, N. A. (2022). Pengaruh Drying Elektroda Low Hydrogen Pada Longitudinal Weld Penstock Material Baja SM 400 B Terhadap Cacat Las Dengan Inspeksi Non destructive Test Metode Radiografi. Journal Of Metallurgical Engineering and Processing Technology, 2(2), 59–65.
Sugihrahma, G. R. (2020). Pengaruh Arus Pengelasan Shield Metal Arc Welding dengan Elektroda E7018 pada Baja Karbon Rendah. JMEMME (Journal of Mechanical Engineering, 4(2), 197–207. https://doi.org/10.31289/jmemme.v4i2.4091
Surono, B., Wahyudi, T. C., Nugroho, E., & Santoso, S. (2023). Pengaruh Jenis Elektroda Pada Sambungan Las Plat Baja Terhadap Kekuatan Tarik Dan Struktur Mikro. 12(02), 363–371.
Susetyo, F. B., Dudung, A., Wiganda, S., Haris, A., & Nugroho, W. (2015). Pengaruh Bentuk Kampuh Terhadap Karakteristik Baja Karbon Rendah Hasil Pengelasan Smaw. Jurnal Konversi Energi Dan Manufaktur, 2(2), 59–64. https://doi.org/10.21009/jkem.2.2.1
Tarkono, G. P. S. Z. (2012). Studi Penggunaan Jenis Elektroda Las Yang Berbeda. Studi Penggunaan Jenis Elektroda Las Yang Berbeda, 3(September), 51–62.
Wahyudi, R. (2019). Analisa Pengaruh Jenis Elektroda Pada Pengelasan SMAW Penyambungan Baja Karbon Rendah Dengan Baja Karbon Sedang Terhadap Tensile Strenght. Journal of Welding Technology, 1(2).
Yunianto, B., Wicaksana, P., Sudharto, J., UNDIP Tembalang, K., & Tengah, J. (2023). Analisis Cacat Hasil Pengelasan Pada Pipa ASTM A106 Grade B Menggunakan Magnetic Particle Test dan Liquid Penetrant Test di Workshop Las dan Inspeksi PPSDM Migas Cepu. Jurnal Rotasi, 25(2), 54–60.
Yusuf Setiawan, M., & Saleh, M. (2024). Analisa Pengaruh Arus & Variasi Jarak Kampuh Las Berdasarkan Kekuatan Uji Tarik & Radiografi Pada Proses Pengelasan Material Baja ASTM A36. Jurnal Ilmiah Multidisiplin, 2(5), 155–170.
Zulfadly, Z., & Ghony, M. A. (2022). Variasi Ampere Terhadap Kekuatan Tarik Pada Hasil Pengelasan Dengan Posisi Down Hand. Hexatech: Jurnal Ilmiah Teknik, 1(01), 39–50. https://doi.org/10.55904/hexatech.v1i01.75
Zulfany, M. D., Erlinawati, Manggala, A., & Pratiwi, I. (2024). Produksi Gas Hidrogen Dengan Proses Elektrolisis Air Laut Ditinjau Dari Konsentrasi KOH. Semantics Schoolar, 9(2), 105–113.
DOI: https://doi.org/10.17509/e.v24i3.87242
Refbacks
- There are currently no refbacks.
Copyright (c) 2025 EDUTECH
Ciptaan disebarluaskan di bawah Lisensi Creative Commons Atribusi-BerbagiSerupa 4.0 Internasional.